Nomen | Gravis Alumina Bricks | ||
LG-0.6 | LG-0.8 | LG-1.0 | |
Mole densitas (g/cm3) | 0.6 | 0.8 | 1.0 |
Frigus comminuens fortitudo (Mpa) ≥ | 1.9 | 2.9 | 4.0 |
Permanens Linearibus Mutatio 1300℃*12h(%) ≤ | 0.5 | 0.5 | 0.5 |
Sceleris ConductivityAverage Temperature 350±25℃ W/(m·K) | ≤0.250 | ≤0.320 | ≤0.450 |
Refractio sub Lond 0.1Mpa (℃) ≥ | 1300 | 1350 | 1380 |
Al2O3(%) ≥ | 50 | 52 | 52 |
Fe2O3(%) ≤ | 1.8 | 1.6 | 1.5 |
Maximum Service Temperature (℃) | 1300 | 1350 | 1380 |
Alumina laterum insulationis vulgo adhibentur pro structura laterum industrialium internis linaturis, ut fornaces furoris, fornaces flatus calidi, culmen fornacis electrici, reverberator, caementum gyratorium fornax et cetera. Praeter altitudinem laterum alumina etiam late adhibentur ut tessellatis regenerativis laterculis, spissamentum continuae emissionis systematis, laterum COLLUM, etc.